Welding Electrode

For Low Carbon Steels:

Cellulose Coated Electrode (E 6010)

(i)                  Lightly coated

(ii)                All Positional, thin brittle slag, highly ductile

Cellulose Coated Electrode (E 7010)

(i)                  It is a cellulose type, all position, friable slag and good penetration

(ii)                Good ductility and creep resistance up to 550c

Rutile Coated Electrode: (E 6012)

(i)                  All positional including vertical down with good penetration

Rutile Coated Electrode: (E 6013) 7411

(i)                  All positional,  medium penetration, low spatter, high deposition rates

Rutile Coated Electrode: (E 6013) 7412

(i)                  All positional included Vertical down, medium penetration

Rutile plus Iron powder coated: (E 7014)

(i)                  All positional, medium heavy coated

(ii)                Iron powder that enables the use of heavy current

(iii)               Deposition efficiency up to 110%

Rutile plus Iron powder coated: (E 7024) 7512K

(i)                  Heavy coated electrodes with high deposition rate

(ii)                Down hand (Butt, Fillet and Horizontal Fillet welds)

(iii)               Easy to manipulate, High welding current can be used

(iv)              Deposition Efficiency is nearly 140%

(v)                It can be used as a Touch electrode

 

Rutile plus Iron powder coated: (E 7024) 7512L

(i)                  Super heavy coated iron powder

(ii)                Metal recovery of about 210%

(iii)               Suitable for high speed welding of down hand, Butt, Fillet and Horizontal  Fillet welds

Acid Coating: (E 6020)

(i)                  Medium heavy coated electrode producing a fluid slag for down hand, horizontal and vertical welding

(ii)                Recommended for low carbon steel where high strength, high quality weld deposits

(iii)               Use for high current and high welding speeds

Basic Coating: (E 7018)

(i)                  Low hydrogen plus iron powder type

(ii)                For heavy joints under restraint and subject to dynamic loading

(iii)               Deposition efficiency 115%

Basic Coating: (E 7018) 1514HJ

(i)                  A medium heavy coated , low hydrogen, iron powder type

(ii)                All position electrode

(iii)               Medium high tensile structural steels

(iv)              1.4% Manganese

(v)                Deposition efficiency 112%

(vi)              Suitable for sub zero  ( 0 ~ -40c)

Basic Coating: (E 7018) 1515HJ

(i)                  Low temperature up to -60c

(ii)                112% metal recovery

Basic Coating: (E 7018-A1)

(i)                  A medium heavy coated all positional

(ii)                Deposition efficiency is 106%